Abstract:
The aim of this research project is to examine the results of using stir casting to incorporate
boron carbide (B4C) and coconut shell ash as reinforcements into an Al1350 alloy (aluminium
wire) matrix. To improve its properties, the hybrid composite was created with a weight
percentage of 1.25. A number of tests are performed, including the Charpy impact test to gauge
the material's impact resistance, microstructure analysis using a Scanning Electron Microscope
(SEM) to examine fractured parts,the Rockwell hardness test, the measurement of grain size and
porosity distribution using an optical microscope, and the electrochemical corrosion test in a
saltwater environment.The findings show that the composite's properties have changed
significantly. Impact energy has been noticeably reduced by 16%, which suggests a decline in
the capacity to withstand sudden impact loads. The corrosion rate has significantly decreased by
26.9%, demonstrating the composite's improved corrosion resistance. A 20% increase in
hardness is also present, indicating increased resistance to localised deformation . Additionally, there is a small 3.7% decrease in density, which suggests a possible weight reduction while
maintaining desired properties. These results contrast with the Al1350 base matrix alloy's
properties. It can be assumed that the base matrix's corrosion resistance and hardness have
improved as a result of the addition of B4C and coconut shell ash reinforcements. However, the
impact strength has slightly decreased.The comprehensive analysis of the composite's properties
can be very advantageous for applications where enhanced corrosion resistance, increased
hardness, and weight reduction are desired